24 COATING SYSTEMS · EXPAND FOR DETAILS
Labels explained
- PLUS
PLUS means additional plasma nitriding before PVD coating (duplex). It supports the PVD coating on through-hardened tool steel. nitriding hardness depth: 0.02–0.05 mm. Depending on the system, PLUS is optional or always included. PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- M-Guard optional
- Additional diffusion treatment for plastics applications. Can be combined with the marked PVD coatings.
- F-series available
- Also available as a separate F variant for specific testing and approval requirements. See the coating details for application areas.
NOVA TiNM-Guard optionalTiNF-series availableAvailable as a Nova serviceHardness in HV: 2300 ± 300Coating thickness in micrometres: 1–6Maximum operating temperature in degrees Celsius: 600
- Composition
- TiN
- Hardness
- 2300 ± 300 HV
- Coating thickness
- 1–6 µm
- Max. operating temperature
- 600 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.5
- Colour
- Gold
- Plus option / duplex
- Not specified
- Finishing as required
- Available
M-Guard for plastics applications
For plastics applications, this coating can be combined with M-Guard as a pretreatment.
Explore M-GuardRecommended applications according to the coating overview
- Metal forming and stamping
- Machining
- Plastics processing
- Decorative applications
F series
NOVA TiN-F
A variant of this coating system for applications with specific testing and approval requirements.
Application areas
- Food
- Packaging
- Medical technology
NOVA CrNM-Guard optionalCrNF-series availableAvailable as a Nova serviceHardness in HV: 2000 ± 250Coating thickness in micrometres: 2–5Maximum operating temperature in degrees Celsius: 700
- Composition
- CrN
- Hardness
- 2000 ± 250 HV
- Coating thickness
- 2–5 µm
- Max. operating temperature
- 700 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.35
- Colour
- Metallic silver
- Plus option / duplex
- Not specified
- Finishing as required
- Available
M-Guard for plastics applications
For plastics applications, this coating can be combined with M-Guard as a pretreatment.
Explore M-GuardRecommended applications according to the coating overview
- Metal forming and stamping
- Plastics processing
F series
NOVA CrN-F
A variant of this coating system for applications with specific testing and approval requirements.
Application areas
- Food
- Packaging
- Medical technology
NOVA CrCNPLUS optionalCrCNAvailable as a Nova serviceHardness in HV: 2300 ± 250Coating thickness in micrometres: 2–8Maximum operating temperature in degrees Celsius: 700
- Composition
- CrCN
- Hardness
- 2300 ± 250 HV
- Coating thickness
- 2–8 µm
- Max. operating temperature
- 700 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.3
- Colour
- Silver grey
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming and stamping
- Machining
DUNOVA 2.0PLUS optionalTiCNAvailable as a Nova serviceHardness in HV: 3700 ± 400Coating thickness in micrometres: 2.5–4.5Maximum operating temperature in degrees Celsius: 400
- Composition
- TiCN
- Hardness
- 3700 ± 400 HV
- Coating thickness
- 2.5–4.5 µm
- Max. operating temperature
- 400 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.2
- Colour
- Silver red
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming and stamping
ALTINOVAAlTiNAvailable as a Nova serviceHardness in HV: 3300 ± 350Coating thickness in micrometres: 2–4Maximum operating temperature in degrees Celsius: 800
- Composition
- AlTiN
- Hardness
- 3300 ± 350 HV
- Coating thickness
- 2–4 µm
- Max. operating temperature
- 800 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.5
- Colour
- Anthracite
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming
- Machining
MULTINOVAPLUS optionalTiAlCNAvailable as a Nova serviceHardness in HV: 3500 ± 400Coating thickness in micrometres: 3.5–5.5Maximum operating temperature in degrees Celsius: 800
- Composition
- TiAlCN
- Hardness
- 3500 ± 400 HV
- Coating thickness
- 3.5–5.5 µm
- Max. operating temperature
- 800 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.25
- Colour
- Salmon red
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming and stamping
MULTINOVA PLUS HTPLUS includedTiAlCNAvailable as a Nova serviceHardness in HV: 3500 ± 400Coating thickness in micrometres: 5.5–8Maximum operating temperature in degrees Celsius: 800
- Composition
- TiAlCN
- Hardness
- 3500 ± 400 HV
- Coating thickness
- 5.5–8 µm
- Max. operating temperature
- 800 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.25
- Colour
- Salmon red
- Plus option / duplex
- Only available with PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming
CRONOVA 2.0PLUS optionalM-Guard optionalAlCrN + dopingAvailable as a Nova serviceHardness in HV: 3300 ± 350Coating thickness in micrometres: 2–5Maximum operating temperature in degrees Celsius: 1100
- Composition
- AlCrN + doping
- Hardness
- 3300 ± 350 HV
- Coating thickness
- 2–5 µm
- Max. operating temperature
- 1100 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.3
- Colour
- Granite grey
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
M-Guard for plastics applications
For plastics applications, this coating can be combined with M-Guard as a pretreatment.
Explore M-GuardRecommended applications according to the coating overview
- Metal forming and stamping
- Machining
- Plastics processing
- Die casting
- Fine blanking
NANONOVAPLUS optionalAlCrTiNAvailable as a Nova serviceHardness in HV: 3300 ± 350Coating thickness in micrometres: 3.5–6Maximum operating temperature in degrees Celsius: 950
- Composition
- AlCrTiN
- Hardness
- 3300 ± 350 HV
- Coating thickness
- 3.5–6 µm
- Max. operating temperature
- 950 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.6
- Colour
- Grey
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming and stamping
- Die casting
InNOVA TOUGH PLUSPLUS includedAlTiCN / TiCNAvailable as a Nova serviceHardness in HV: 3700 ± 400Coating thickness in micrometres: 5.5–8Maximum operating temperature in degrees Celsius: 400
- Composition
- AlTiCN / TiCN
- Hardness
- 3700 ± 400 HV
- Coating thickness
- 5.5–8 µm
- Max. operating temperature
- 400 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.2
- Colour
- Silver grey
- Plus option / duplex
- Only available with PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming
InNOVA TOUGH BLACK PLUSPLUS includedAlTiCN / TiCN / DLCAvailable as a Nova serviceHardness in HV: 3700 ± 400Coating thickness in micrometres: 5.5–8Maximum operating temperature in degrees Celsius: 400
- Composition
- AlTiCN / TiCN / DLC
- Hardness
- 3700 ± 400 HV
- Coating thickness
- 5.5–8 µm
- Max. operating temperature
- 400 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.15
- Colour
- Black
- Plus option / duplex
- Only available with PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming
InNOVA FPLUS optionalCrAlN-basedAvailable as a Nova serviceHardness in HV: 3200 ± 400Coating thickness in micrometres: 5–10Maximum operating temperature in degrees Celsius: 900
- Composition
- CrAlN-based
- Hardness
- 3200 ± 400 HV
- Coating thickness
- 5–10 µm
- Max. operating temperature
- 900 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.3
- Colour
- Silver grey
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming
- Die casting
DUNOVA BLACKTiCN / DLCAvailable as a Nova serviceHardness in HV: 3700 ± 400Coating thickness in micrometres: 2.5–4.5Maximum operating temperature in degrees Celsius: 400
- Composition
- TiCN / DLC
- Hardness
- 3700 ± 400 HV
- Coating thickness
- 2.5–4.5 µm
- Max. operating temperature
- 400 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.15
- Colour
- Black
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming and stamping
NOVA ta-Cta-C, 80 % sp³Available as a Nova serviceHardness in HV: 5500–6000Coating thickness in micrometres: 0.3–1.2Maximum operating temperature in degrees Celsius: 500
- Composition
- ta-C, 80 % sp³
- Hardness
- 5500–6000 HV
- Coating thickness
- 0.3–1.2 µm
- Max. operating temperature
- 500 °C
- Coating temperature
- 120 °C
- Coefficient of friction
- 0.1
- Colour
- Rainbow to grey
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming
- Machining
- Stamping of non-ferrous metals
DIANOVA CM-Guard optionalCrN / DLC a-C:H:MeAvailable as a Nova serviceHardness in HV: 1500–2300Coating thickness in micrometres: 2.5–6Maximum operating temperature in degrees Celsius: 350
- Composition
- CrN / DLC a-C:H:Me
- Hardness
- 1500–2300 HV
- Coating thickness
- 2.5–6 µm
- Max. operating temperature
- 350 °C
- Coating temperature
- 180 °C
- Coefficient of friction
- 0.15
- Colour
- Black grey
- Plus option / duplex
- Not specified
- Finishing as required
- Available
M-Guard for plastics applications
For plastics applications, this coating can be combined with M-Guard as a pretreatment.
Explore M-GuardRecommended applications according to the coating overview
- Metal forming and stamping
- Machining
- Machine parts and components
- Decorative applications
- Plastics processing
DIANOVADLC a-C:HAvailable as a Nova serviceHardness in HV: 2500 ± 300Coating thickness in micrometres: 1–3Maximum operating temperature in degrees Celsius: 350
- Composition
- DLC a-C:H
- Hardness
- 2500 ± 300 HV
- Coating thickness
- 1–3 µm
- Max. operating temperature
- 350 °C
- Coating temperature
- 160–200 °C
- Coefficient of friction
- 0.1–0.2
- Colour
- Black grey
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Metal forming
- Machining
- Decorative applications
ALSINOVA CUT 2.0AlTiSiN-basedAvailable as a Nova serviceHardness in HV: 3800 ± 400Coating thickness in micrometres: 1–3Maximum operating temperature in degrees Celsius: > 1100
- Composition
- AlTiSiN-based
- Hardness
- 3800 ± 400 HV
- Coating thickness
- 1–3 µm
- Max. operating temperature
- > 1100 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.5
- Colour
- Orange brown
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Machining
InNOVA Micral CUTMicro AlloyedAvailable as a Nova serviceHardness in HV: 3300 ± 250Coating thickness in micrometres: 1–3Maximum operating temperature in degrees Celsius: 1100
- Composition
- Micro Alloyed
- Hardness
- 3300 ± 250 HV
- Coating thickness
- 1–3 µm
- Max. operating temperature
- 1100 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.5
- Colour
- Dark grey
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Machining
InNOVA Micral Titan CUTMicro AlloyedAvailable as a Nova serviceHardness in HV: 3500 ± 250Coating thickness in micrometres: 1–3Maximum operating temperature in degrees Celsius: 1100
- Composition
- Micro Alloyed
- Hardness
- 3500 ± 250 HV
- Coating thickness
- 1–3 µm
- Max. operating temperature
- 1100 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.5
- Colour
- Brown
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Machining
MP-CUTAlTiCrN-basedAvailable as a Nova serviceHardness in HV: 3300 ± 400Coating thickness in micrometres: 1–3Maximum operating temperature in degrees Celsius: 1100
- Composition
- AlTiCrN-based
- Hardness
- 3300 ± 400 HV
- Coating thickness
- 1–3 µm
- Max. operating temperature
- 1100 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.5
- Colour
- Anthracite
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Machining
Drill CUTAlTiSiN-basedAvailable as a Nova serviceHardness in HV: 3800 ± 400Coating thickness in micrometres: 1–5Maximum operating temperature in degrees Celsius: > 1100
- Composition
- AlTiSiN-based
- Hardness
- 3800 ± 400 HV
- Coating thickness
- 1–5 µm
- Max. operating temperature
- > 1100 °C
- Coating temperature
- 450–480 °C
- Coefficient of friction
- 0.5
- Colour
- Dark brown
- Plus option / duplex
- Not specified
- Finishing as required
- Available
Recommended applications according to the coating overview
- Machining
TOPNOVAPLUS optionalM-Guard optionalTiAlNAvailable as a Nova serviceHardness in HV: 2800 ± 400Coating thickness in micrometres: 2–8Maximum operating temperature in degrees Celsius: 700
- Composition
- TiAlN
- Hardness
- 2800 ± 400 HV
- Coating thickness
- 2–8 µm
- Max. operating temperature
- 700 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.5
- Colour
- Aubergine
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
M-Guard for plastics applications
For plastics applications, this coating can be combined with M-Guard as a pretreatment.
Explore M-GuardRecommended applications according to the coating overview
- Metal forming
- Plastics processing
- Die casting
InNOVA PMPLUS optionalM-Guard optionalCrN / CrONAvailable as a Nova serviceHardness in HV: 2500 ± 400Coating thickness in micrometres: 2–8Maximum operating temperature in degrees Celsius: 700
- Composition
- CrN / CrON
- Hardness
- 2500 ± 400 HV
- Coating thickness
- 2–8 µm
- Max. operating temperature
- 700 °C
- Coating temperature
- 450–500 °C
- Coefficient of friction
- 0.3
- Colour
- Rainbow
- Plus option / duplex
- Available with or without PLUS
- PLUS is used for stamping, forming and die casting. Through-hardened tool steels with a tempering temperature above 500 °C are required.
- Finishing as required
- Available
M-Guard for plastics applications
For plastics applications, this coating can be combined with M-Guard as a pretreatment.
Explore M-GuardRecommended applications according to the coating overview
- Metal forming
- Plastics processing
- Food
- Packaging
- Decorative applications
InNOVA M-GuardDiffusion treatmentFor plastics applications only · with or without a PVD coatingAvailable as a Nova serviceHardness in HV: up to 1400Coating thickness in micrometres: No separate coatingMaximum operating temperature in degrees Celsius: depending on heat treatment
- Composition
- Diffusion treatment
- Hardness
- up to 1400 HV
- Coating thickness
- No separate coating
- Max. operating temperature
- depending on heat treatment
- Treatment temperature
- 380–440 °C
- Coefficient of friction
- 0.6
- Colour
- Metallic silver
- Finishing as required
- Available
Recommended applications according to the coating overview
- Plastics processing
6 / 24
Technical guidance based on the NOVA coating overview and Apex datasheets. Properties depend on the system and application. We confirm suitability and current specifications with you.
Open the Nova service portfolio as an image ↗